Browsing by Author "Wang, Zhonglin"

Now showing 1 - 2 of 2
  • Thumbnail Image
    ItemOpen Access
    Phase-transition induced giant negative electrocaloric effect in a lead-free relaxor ferroelectric thin film
    (Royal Society of Chemistry, 2019-05-02) Peng, Biaolin; Zhang, Qi; Gang, Bai; Leighton, Glenn J. T.; Shaw, Christopher; Milne, Steven J.; Zou, Bingsuo; Sun, Wenhong; Huang, Haitao; Wang, Zhonglin
    Ferroelectric/antiferroelectric thin/thick films with large positive or negative electrocaloric (EC) effects could be very useful in designing commercial refrigeration devices. Here, a giant negative EC effect (maximum ΔT ∼ −42.5 K with ΔS ∼ −29.3 J K−1 kg−1) comparable to the best positive EC effects reported so far is demonstrated for 0.5(Ba0.8Ca0.2)TiO3–0.5Bi(Mg0.5Ti0.5)O3 (BCT–BMT) lead-free relaxor ferroelectric thin films prepared on Pt(111)/TiOx/SiO2/Si substrates using a sol–gel method. An electric-field induced structural phase transition (nanoscale tetragonal and orthorhombic to rhombohedral) along the out-of-plane [111] direction plays a very key role in developing the giant negative EC effect. This breakthrough will pave the way for practical applications of next-generation refrigeration devices with high cooling efficiency in one cycle by ingeniously utilizing and combining both the giant negative and positive EC effects. Moreover, a large energy density of 51.7 J cm−3 with a high power density of 1.15 × 1010 W kg−1 at room temperature is also achieved in the thin film, indicating that it is also an attractive multifunctional material for energy storage.
  • Thumbnail Image
    ItemOpen Access
    Thermal strain induced large electrocaloric effect of relaxor thin film on LaNiO3/Pt composite electrode with the coexistence of nanoscale antiferroelectric and ferroelectric phases in a broad temperature range
    (Elsevier, 2018-03-08) Peng, Biaolin; Zhang, Qi; Lyu, Yinong; Liu, Laijun; Lou, Xiaojie; Shaw, Christopher; Huang, Haitao; Wang, Zhonglin
    Ferroelectric/antiferroelectric thin/thick films with large electrocaloric (EC) effect in a broad operational temperature range are very attractive in solid-state cooling devices. We demonstrated that a large positive electrocaloric (EC) effect (maximum ΔT ~ 20.7 K) in a broad temperature range (~ 110 K) was realized in Pb0.97La0.02(Zr0.65Sn0.3Ti0.05)O3 (PLZST) relaxor antiferroelectric (AFE) thin film prepared using a sol-gel method. The large positive EC effect may be ascribed to the in-plane residual thermal tensile stress during the layer-by-layer annealing process, and the high-quality film structure owing to the utilization of the LaNiO3/Pt composite bottom electrode. The broad EC temperature range may be ascribed to the great dielectric relaxor dispersion around the dielectric peak because of the coexistence of nanoscale multiple FE and AFE phases. Moreover, a large pyroelectric energy density (6.10 Jcm−3) was harvested by using an Olsen cycle, which is much larger than those (usually less than 10− Jcm−3) obtained by using direct thermal-electrical, Stirling and Carnot cycles, etc. These breakthroughs enable the PLZST thin film an attractive multifunctional material for applications in modern solid-state cooling and energy harvesting.