Effect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy

Simple item page
dc.contributor.authorZhang, Tao
dc.contributor.authorQin, Zhen-yang
dc.contributor.authorGong, Hai
dc.contributor.authorWu, Yun-xin
dc.contributor.authorChen, Xin
dc.date.accessioned2024-08-28T11:03:15Z
dc.date.available2024-08-28T11:03:15Z
dc.date.freetoread2025-08-14
dc.date.issued2024-07
dc.date.pubOnline2024-08-13
dc.description.abstractWire-arc additive manufacture (WAAM) has great potential for manufacturing of Al-Cu components. However, inferior mechanical properties of WAAM deposited material restrict its industrial application. Inter-layer cold rolling and thermo-mechanical heat treatment (T8) with pre-stretching deformation between solution and aging treatment were adopted in this study. Their effects on hardness, mechanical properties and microstructure were analyzed and compared to the conventional heat treatment (T6). The results show that cold rolling increases the hardness and strengths, which further increase with T8 treatment. The ultimate tensile strength (UTS) of 513 MPa and yield stress (YS) of 413 MPa can be obtained in the inter-layer cold-rolled sample with T8 treatment, which is much higher than that in the as-deposited samples. The cold-rolled samples show higher elongation than that of as-deposited ones due to significant elimination of porosity in cold rolling; while both the T6 and T8 treatments decrease the elongation. The cold rolling and pre-stretching deformation both contribute to the formation of dense and dispersive precipitated θ′ phases, which inhibits the dislocation movement and enhances the strengths; as a result, T8 treatment shows better strengthening effect than the T6 treatment. The strengthening mechanism was analyzed and it was mainly related to work hardening and precipitation strengthening.
dc.description.journalNameJournal of Central South University
dc.description.sponsorshipProject(ZZYJKT2024-08) supported by the State Key Laboratory of Precision Manufacturing for Extreme Service Performance, China; Project(2022JB11GX004) supported by Selection of the best Candidates to Undertake Key Research Projects by Dalian City, China; Project(201806835007) supported by China Scholarship Council
dc.format.extent2181-2193
dc.identifier.citationZhang T, Qin Z-Y, Gong H, et al., (2024) Effect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy. Journal of Central South University, Volume 31, Issue 7, July 2024, pp. 2181-2193
dc.identifier.eissn2227-5223
dc.identifier.elementsID551802
dc.identifier.issn2095-2899
dc.identifier.issueNo7
dc.identifier.urihttps://doi.org/10.1007/s11771-024-5740-2
dc.identifier.urihttps://dspace.lib.cranfield.ac.uk/handle/1826/22832
dc.identifier.volumeNo31
dc.languageEnglish
dc.language.isoen
dc.publisherSpringer
dc.publisher.urihttps://link.springer.com/article/10.1007/s11771-024-5740-2
dc.rightsNo licence
dc.subject4014 Manufacturing Engineering
dc.subject40 Engineering
dc.titleEffect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy
dc.typeArticle
dcterms.dateAccepted2024-01-11

Files

Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Effect_of_thermo-mechanical_treatment-2024.pdf
Size:
3.98 MB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.63 KB
Format:
Plain Text
Description:
Download

Collections

Staff publications (SATM)